Cast iron base for testing machine 2000×1000mm, vibration damping platform for material testing machines.

Analysis of Design and Function of Testing Machine Cast Iron Base
The cast iron base of a testing machine serves as the "stable foundation" for various types of testing machines such as tension, compression, and fatigue testers. Its design rationality directly determines the measurement accuracy, operational stability, and service life of the testing machine. As a core component that supports the main unit of the testing machine, the workpiece under test, and dynamic loading forces, the cast iron base must meet multiple requirements including strength, vibration resistance, and precision retention. Through scientific structural design and material selection, it provides the underlying guarantee for the reliability of test data. This article analyzes the design logic and practical value of the testing machine cast iron base from four dimensions: design principles, key structures, core functions, and application adaptability. Design Logic and Practical Value.

I. Core Design Principles: Centered on the Three Goals of "Stability, Vibration Resistance, and Precision"
The design of the testing machine cast iron base must closely align with the requirements of the testing scenario, adhering to three core principles to avoid test errors caused by design issues:
Strength Matching Principle: The rated load capacity of the base must be ≥ 1.2 times the weight of the testing machine + the weight of the test piece + the dynamic loading force. The material tensile strength must be ≥ 300 MPa (HT250 gray cast iron for light-load testing machines, HT300 or QT600 ductile cast iron for medium to heavy loads), ensuring no deformation during dynamic loading;
Vibration Resistance Priority Principle: Through material damping characteristics and structural optimization, absorb vibrations generated during testing in the 5-2000 Hz range. The damping ratio must be ≥ 0.03, and vibration transmissibility ≤ 15%, to avoid vibration interference with sensor readings;
Precision Retention Principle: After double aging treatment (550°C high-temperature aging + 6 months natural aging), the residual stress removal rate must be ≥ 85%, and annual precision attenuation ≤ 0.002 mm/m, ensuring no baseline drift after long-term use.
II. Key Structural Design: Optimization from Material to Structure
1. Material Selection: Cast Iron as the Core, Strength Adapted as Needed
Light-load testing machines (loading force ≤ 50 kN, e.g., electronic tensile testing machines): Use HT250 gray cast iron, with moderate cost, damping ratio of 0.03-0.04, meeting conventional vibration resistance needs;
Medium to heavy-load testing machines (loading force 50-500 kN, e.g., hydraulic testing machines): Use HT300 gray cast iron, with tensile strength ≥ 300 MPa and compressive strength ≥ 900 MPa, suitable for medium dynamic loading;
Heavy-load/high-frequency testing machines (loading force > 500 kN or vibration frequency > 500 Hz, e.g., fatigue testing machines): Use QT600 ductile cast iron, with tensile strength ≥ 600 MPa and damping ratio of 0.04-0.05, offering superior vibration resistance and deformation resistance.
2. Structural Design: Rib Layout + Reference Surface Machining is Key
Rib Layout: Adopt a "cross-rib + box-type main body" design, with rib thickness of 12-15 mm and spacing of 200-250 mm, forming a dense support network. This increases torsional stiffness by 40% compared to flat plate structures, with a deflection ≤ 0.02 mm when a 2000×3000 mm base carries a 50 kN load;
Reference Surface Machining: The worktable undergoes three processes: rough grinding → fine grinding → ultra-fine grinding, with flatness error ≤ 0.05 mm/m (Grade 0 precision) and surface roughness Ra1.6-3.2 μm, ensuring levelness error ≤ 0.01 mm/m after installation of the testing machine main unit;
The design and function of the testing machine cast iron base are essentially a combination of "structure adapting to needs and material supporting performance." Through scientific material selection, rational rib layout, and high-precision reference machining, the base not only meets the load-bearing and positioning requirements of the testing machine but also ensures the accuracy of test data through vibration resistance and damping functions, providing stable support for scenarios such as material testing and component reliability verification. In the current pursuit of test accuracy and efficiency, the cast iron base has become an indispensable core component of testing machines, directly impacting the credibility of test results and the R&D and production efficiency of enterprises.